Color and Translucency Variation of a One-Shaded Resin-Based Composite after Repeated Heating Cycles and Staining

Background: This study aimed to determine the effect of repeated pre-polymerization heating on the color and translucency of a one-shaded resin-based composite and to evaluate whether the heating cycles affect its color stability. (2) Methods: Fifty-six samples of 1-mm thickness were fabricated from Omnichroma (OM) after applying different heating cycles (for one, five, and ten times at 45 C) before polymerization (n = 14/group) and afterwards were stained with a yellow dye solution. CIE L*, a*, b*, C*, h coordinates were recorded, and color differences, whiteness, and translucency were calculated, before and after staining. (3) Results: Heating cycles significantly influenced the color coordinates, WID00, and TP00 of OM being higher after one heating cycle and decreasing as the number of heating cycles increased. The color coordinates, WID, and TP00 after staining significantly differed for each group. The color and whiteness differences calculated after staining exceeded the acceptability thresholds for all groups. The color and whiteness variations after staining were clinically unacceptable. (4) Conclusions: Repeated pre-polymerization heating induces a clinically acceptable color and translucency change to OM. Although the color changes resulting after staining are clinically unacceptable, increasing the number of heating cycles up to ten times slightly reduces the color differences.Research Project PCD 1032/55 from the Iuliu Hatieganu University of Medicine and Pharmacy, Cluj-Napoca, Romani

The Impact of Simulated Bruxism Forces and Surface Aging Treatments on Two Dental Nano-Biocomposites—A Radiographic and Tomographic Analysis

Background and Objectives: Nowadays, indication of composite materials for various clinical situations has increased significantly. However, in the oral environment, these biomaterials are subjected (abnormal occlusal forces, external bleaching, consumption of carbonated beverages, etc.) to changes in their functional and mechanical behavior when indicated primarily for patients with masticatory habits. The study aimed to recreate in our lab one of the most common situations nowadays—in-office activity of a young patient suffering from specific parafunctional occlusal stress (bruxism) who consumes acidic beverages and is using at-home dental bleaching. Materials and Methods: Sixty standardized class II cavities were restored with two nanohybrid biocomposite materials (Filtek Z550, 3M ESPE, and Evetric, Ivoclar Vivadent); the restored teeth were immersed in sports drinks and carbonated beverages and exposed to an at-home teeth bleaching agent. The samples were subjected to parafunctional mechanical loads using a dual-axis chewing simulator. A grading evaluation system was conducted to assess the defects of the restorations using different examination devices: a CBCT, a high-resolution digital camera, and periapical X-rays. Results: Before mechanical loading, the CBCT analysis revealed substantially fewer interfacial defects between the two resin-based composites (p > 0.05), whereas, after bruxism forces simulation, significantly more defects were identified (p Conclusions: There were different behaviors observed regarding the studied nanocomposites when simulation of parafunctional masticatory forces was associated with aging treatments